Solvent Based 2 Component PU Resin
Synthetic Leather & Split Leather | |||||||
Articles | Viscosity (cps/25℃) | Nonvolatile | 100% Modulus (kg/cm2) | Tensile Strength (kg/cm2) | Elongation (%) | Solvents | Characteristics |
SA-2036HR | 50,000~80,000 | 40±2 | 20~30 | >150 | >300 | DMF、MEK | Pre-drying grade、good hydrolysis resistance、good adhesive strength |
SA-2060HR | 80,000~110,000 | 60±2 | 15~35 | >250 | >350 | DMF、MEK、EAC | Good hydrolysis resistance、good adhesive strength |
SA-2170HR | 60,000~90,000 | 70±1 | 15~25 | >200 | >250 | DMF、MEK、DMC | Long pot-life |
SA-2321HR | 90,000~110,000 | 60±2 | 20~40 | >150 | >250 | DMF、MEK | Good hydrolysis resistance、excellent flexibility |
SA-6010P | 80,000~120,000 | 60±2 | 16~32 | >120 | >300 | DMF、TOL | Pre-drying grade、excellent flexibility at low temperature、quick setting type |
SA-6030P | 100,000~140,000 | 60±2 | 16~32 | >120 | >300 | DMF、TOL、MEK | Pre-drying grade、excellent flexibility at low temperature、quick setting type、Economic grade |
SA-3064HR | 40,000~70,000 | 50±1 | 17~27 | >150 | >300 | DMF、TOL、MEK | Pre-drying grade、good hydrolysis resistance、excellent flexibility at low temperature |
Textile Coating | |||||||
Articles | Viscosity (cps/25℃) | Nonvolatile | 100% Modulus (kg/cm2) | Tensile Strength (kg/cm2) | Elongation (%) | Solvents | Characteristics |
SA-2018MP | 30,000~50,000 | 45±1 | 10~20 | >25 | >300 | DMF TOL MEK | Water proof and excellent moisture permeable |
SA-2019MP | 60,000~80,000 | 45±1 | 15~25 | >100 | >300 | DMF TOL MEK | Water proof and excellent moisture permeable |
SA-2021MP-1 | 60,000~80,000 | 45±1 | 13~27 | >100 | >300 | DMF TOL | Water proof and good moisture permeable |
SA-2020MP | 50,000~80,000 | 45±1.5 | 15~30 | >100 | >300 | DMF TOL | Water proof and excellent moisture permeable |
SA-2130M | 60,000~80,000 | 30±11.5 | 10~20 | >100 | >400 | DMF TOL | Economic grade、compatible with acrylic resin |
SA-215 | 80,000~120,000 | 45±1 | 10~30 | >150 | >500 | DMF TOL MEK | Soft grade |
SA-360 | 80,000~110,000 | 35±1 | 30~50 | >150 | >350 | TOL MEK | Primer for PVC coating、medium hard grade |
SA-390 | 60,000~100,000 | 35±1 | 35~55 | >150 | >350 | DMF TOL MEK | Primer for PVC coating、medium hard grade |
SA-2265 | 95,000~125,000 | 65±1 | 20~40 | >150 | >250 | DMF TOL MEK | High solid content、long pot-life |
SA-6066 | 115,000~145,000 | 65±1 | 17~33 | >200 | >350 | DMF TOL MEK | Soft grade、High solid content |
SA-2260LE | 120,000~150,000 | 60±2 | 20~40 | >200 | >300 | MEK EAc | Good green strength、good adhesive strength |
SA-22N | 100~200 | 24.5±1 | - | - | - | EAC TOL MEK | Adhesive for spray、good hot hydrolysis and DOP resistance、long tackiness、yellowing resistance |