Thermoplastic polyurethane TPU
Properties | Units | Test Method | EMH-85A | EMH-90A | EMH-95A | EMH-98A | EMH-64D |
|---|---|---|---|---|---|---|---|
Hardness | Shore A | DIN-53505 | 85±2 | 90±2 | 95±2 |
|
|
Shore D | DIN-53506 |
|
|
| 56±2 | 64±2 | |
Tensile Strength | Kg/cm2 | DIN-53504 | >310 | >320 | >340 | >350 | >320 |
Elongation | % | DIN-53504 | >450 | >420 | >370 | >340 | >310 |
Tear Strength | Kg/cm | DIN-53515 | >80 | >100 | >120 | >140 | >150 |
100% Modulus | Kg/cm2 | DIN-53504 | >45 | >60 | >80 | >100 | >140 |
Melt Flow Index | g/10min | DIN 53735 | 15±5 @185℃ | 20±5@190℃ | 20±5@190℃ | 20±5@195℃ | 25±5@190℃ |
Recommended Drying Condition | 90~110℃/3hr | ||||||
Recommended Processing Temp | 180~195℃ | 180~195℃ | 185~200℃ | 190~205℃ | 190~210℃ | ||
Advantage | Good Elasticity、Wide Processing Range、Good Flow Ability | ||||||
Applications | Air Hose、Gardening Hose、Oil Pipeline、Wire and Cable | ||||||
Properties | Units | Test Method | EMS-65A | EME-75A | EME-80A | EME-85A | EME-90A | EME-95A | |
|---|---|---|---|---|---|---|---|---|---|
Hardness | Shore A | DIN-53505 | 67±3 | 75±3 | 80±2 | 85±2 | 90±2 | 95±2 | |
Shore D | DIN-53506 |
|
|
|
|
|
| ||
Tensile Strength | Kg/cm2 | DIN-53504 | >150 | >190 | >280 | >300 | >330 | >360 | |
Elongation | % | DIN-53504 | >500 | >600 | >450 | >400 | >400 | >400 | |
Tear Strength | Kg/cm | DIN-53515 | >50 | >50 | >55 | >60 | >80 | >100 | |
100% Modulus | Kg/cm2 | DIN-53504 | >20 | >30 | >35 | >45 | >65 | >75 | |
Melt Flow Index | g/10min | DIN 53735 | 30±5 @185℃ | 20±5 @170℃ | 15±5 @190℃ | 20±5 @193℃ | 25±5 @205℃ | 20±5 @205℃ | |
Recommended Drying Condition | 90~110℃/3hr | ||||||||
Recommended Processing Temp | 175~190℃ | 175~190℃ | 175~190℃ | 180~195℃ | 180~195℃ | 185~200℃ | |||
Advantage | NoMigration、Good Elasticity、Wide Processing Range | ||||||||
Applications | Shoe Parts、Mechanical Parts、Watch Belt、3C Product | ||||||||
Properties | Units | Method | EMP- 80A | EMP- 85A | EMP- 90A | EMP- 95A | EMP- 98A | EMP- 60D | EMP- 64D | EMP- 71D |
|---|---|---|---|---|---|---|---|---|---|---|
Hardness | Shore A | DIN-53505 | 80±2 | 85±2 | 90±2 | 95±2 |
|
|
|
|
Shore D | DIN-53506 |
|
|
|
| 55±2 | 60±2 | 64±2 | 70±2 | |
Tensile Strength | Kg/cm2 | DIN-53504 | >280 | >300 | >320 | >355 | >380 | >400 | >420 | >430 |
Elongation | % | DIN-53504 | >450 | >450 | >400 | >400 | >385 | >350 | >350 | >300 |
Tear Strength | Kg/cm | DIN-53515 | >55 | >75 | >85 | >100 | >130 | >130 | >155 | >165 |
100% Modulus | Kg/cm2 | DIN-53504 | >30 | >40 | >60 | >90 | >130 | >140 | >165 | >205 |
Melt Flow Index | g/10min | DIN 53735 | 25±5 @190℃ | 20±5 @195℃ | 30±5 @205℃ | 20±5 @207℃ | 20±5 @213℃ | 20±5 @217℃ | 30±10 @219℃ | 20±5 @222℃ |
Recommended Drying Condition | 90~110℃/3hr | |||||||||
Recommended Processing Temp | 175~190℃ | 180~195℃ | 180~195℃ | 185~200℃ | 185~200℃ | 190~205℃ | 195~210℃ | 195~215℃ | ||
Advantage | Good abrasion Resistance、Wide Processing Range、Good Heat Resistance、High physical property Performance | |||||||||
Applications | Shoe Sole、Shoe buckle、Accessory、Industrial Casters、Watch Belt、Toys、Luggage Wheel | |||||||||
Properties | Units | Test Method | EMM-75A | EMM-80A | EMM-85A | EMM-95A | EMM-98AE | EMM-90A2 | |
|---|---|---|---|---|---|---|---|---|---|
Hardness | Shore A | DIN-53505 | 75±3 | 80±3 | 85±2 | 95±2 |
| 90±2 | |
Shore D | DIN-53506 |
|
|
|
| 56±2 |
| ||
Tensile Strength | Kg/cm2 | DIN-53504 | >150 | >200 | >230 | >300 | >300 | >270 | |
Elongation | % | DIN-53504 | >600 | >600 | >500 | >450 | >350 | >500 | |
Tear Strength | Kg/cm | DIN-53515 | >50 | >60 | >60 | >80 | >90 | >85 | |
100% Modulus | Kg/cm2 | DIN-53504 | >28 | >35 | >35 | >80 | >90 | >40 | |
300% Modulus | Kg/cm2 | DIN-53504 | >40 | >60 | >65 | >130 | >180 | >100 | |
Recommended Drying Condition | 80~100℃/3hr | ||||||||
Recommended Processing Temp | 175~190℃ | 185~200℃ | 195~210℃ | ||||||
Advantage | Excellent Hydrolysis Resistance ,Good Elasticity、Wide Processing Range、Good Flow Ability | Excellent Hydrolysis Resistance, Good Elasticity | |||||||
Applications | Air Hose、Gardening Hose、Oil Pipeline、Wire and Cable | Mechanical Parts、Injection Parts | |||||||
Properties | Units | Test Method | EMK-75A | EMK-85A |
|---|---|---|---|---|
Density | g/cm3 | DIN 53479 | 1.17-1.22 | 1.17-1.22 |
Hardness | Shore A | DIN 53505 | 75±3 | 85±3 |
Flow beginning temperature | ℃ | SHIMADZU JIS K 7311 | 110-114 | 132-136 |
Melt Flow Index | g/10min | DIN 53735 | 18±3 (177℃2.16kg) | 18±3 (177℃2.16kg) |
Applications | Hot melt adhesive film, sealing tape, textile lamination | |||
Properties | Units | Test Method | EME-90ACL | EME-90ACH | EME-85ACL | EME-75ACL |
|---|---|---|---|---|---|---|
Density | g/cm3 | DIN 53479 | 1.20-1.24 | 1.20-1.24 | 1.20-1.24 | 1.20-1.24 |
Hardness | Shore A | DIN 53505 | 90±2 | 90±2 | 85±3 | 75±3 |
Tensile Strength | kg/cm2 | DIN 53504 | >300 | >240 | >250 | >180 |
100% Modulus | kg/cm2 | DIN 53504 | >70 | >70 | >35 | >30 |
300% Modulus | kg/cm2 | DIN 53504 | >110 | >100 | >70 | >50 |
Elongation | % | DIN 53504 | >500 | >500 | >500 | >600 |
Tear Strength | kg/cm | DIN 53515 | >110 | >90 | >60 | >60 |
Melt Flow Index | g/10min | DIN 53735 | 25±5 (185℃8.7kg) | 90±20 (185℃8.7kg) | 25±5 (185℃8.7kg) | 70±10 (185℃8.7kg) |
Processing Roller temperature | ℃ |
| 150~160 | 150~160 | 145~160 | 125~140 |
Applications | Film,FoamingFilm,leather, | |||||